TJPC 1723

 

TJPC 1723 

 TJPC 1723

 

1 product description

TJPC 1723 is an emulsion styrene-butadiene rubber obtained by cold polymerization using mixture of rosin acid and fatty acid soaps as emulsifiers, contains 23.5% of chemically bonded styrene. It is plasticized with 37.5 parts of TDAE oil (extender oil with reduced content of polycyclic aromatics) which does comply with EU DIRECTIVE 2005/69/EC for use in tires within the EU. A phenolic antioxidant is added during the production process.

2 applications

The main application is tire production. It can be processed in all sectors of the tire and rubber industry.

3 CHARACTERSTICS

TJPC 1723 is a general purpose rubber characterized by good process ability, mechanical properties and abrasion resistance. Due to the lower oil Tg, it shows a slight advantage in rolling resistance performance compared to TJPC 1712.

4 PACKAGING – TRANSPORTATION – STORAGE

35 ±0.5 KG bales wrapped with polyethylene film.

36 bales per crate (1260±18 KG).

TJPC 1723 is typically transported in covered road trucks, in covered railway carriages and in standard shipping containers. TJPC 1723 is not a dangerous material to transport.

Product should be stored in sheltered conditions away from direct sunlight away from radiant heating elements and the temperature should not exceed 30°C.

Typical Properties Units Values Test method
Raw Mooney Viscosity MU 42-52 ASTM D1646
Volatile Material % wt < 0.75 ASTM D5668
Ash Content % wt < 0.5 ASTM D5667
Organic acids % wt 3.9 -5.7 ASTM D5774
Soaps % wt < 0.5 ASTM D5774
Bounded styrene % wt 22.5-24.5 ASTM D5775
Oil Content % wt 25.8-28.8 ASTM D5775
Compound Mooney viscosity2 MU <62 ASTM D1646
Tensile strength (35 min cured)2 kg/cm2 >200 ASTM D 412
Ultimate elongation (35 min cured)2 % >530 ASTM D 412
300 % Modulus (35 min cured)2 kg/cm2 79-109 ASTM D 412
pic