TJPC 1712

 

TJPC 1712 

 TJPC 1712

 

1 product description

Styrene-Butadiene Rubber “TJPC 1712” is produced by a technology of cold emulsion copolymerization based on soaps of rosin and fatty acids and contains 23.5% of chemically bonded styrene and extended with 37.5 parts highly aromatic oil. It is coagulated by a system of acid and synthetic coagulant. The rubber is protected by stabilizer system.

2 applications

Application possibilities for TJPC 1712 include tire and mechanical goods compounds where color and staining are not decisive factors.CHARACTERSTICS

3 CHARACTERSTICS

Raw materials for this product are carefully chosen for the best physical properties.TJPC 1712 has very good properties such as processability, abrasion resistance, less tendency to scorching processing.

Typical Properties  Units Values Test method
Raw Mooney viscosity MU 42-52 ASTM D1646
Volatile Material % wt < 0.75 ASTM D5668
Ash Content % wt < 1 ASTM D5667
Organic acids % wt 3.9 -5.7 ASTM D5774
Soaps % wt < 0.5 ASTM D5774
Bounded styrene % wt 22.5-24.5 ASTM D5775
Oil Content % wt 25.8-28.8 ASTM D5775
Compound Mooney viscosity2 MU <62 ASTM D1646
Tensile strength (35 min cured)2 kg/ cm2 >200 ASTM D 412
Ultimate elongation (35 min cured)2 % >530 ASTM D 412
300 % Modulus (35 min cured)2 kg/ cm2 79-109 ASTM D 412

1 The above data is only a typical value and to each shipping lot/ delivery a quality certificate including data on properties of the product determined during release control is issued. Scope of the testing which is covered by the quality certificate is each time agreed upon in the sales contract.

2 Compounding according ASTM D-3182 & D-3185.