General

Mooney Viscosity

ASTM D1646

MPP16

ML1+4 @ 100°C

50 – 60

Bound Styrene

ASTM D5775

MPP5-MPP6

wt %

N/A

Block styrene

ASTM D3314

MPP8

wt %

N/A

Solution viscosity*

ASTM D5774

MPP9

cPs

N/A

Gel content

MPP12

arbitrary

N/A

Molecular weight

MPP1

KDalton

N/A

Coupling efficiency

MPP1

%

N/A

Volatile matter content

ASTM D5668

MPP10

wt %

0.6 max

Residual solvent

MPP18

ppm

N/A

Colour

ASTM E313

MPP13

Yellow index

N/A

Solution color (Pt/Co)

ASTM D1209

arbitrary

N/A

Vinyl content

MPP5-MPP6

wt % on butadiene

11 – 13

Ash content

ASTM D5667

MPP15

wt %

0.08

Solvent extractables

ASTM D5774

MPP11

wt %

N/A

General

Mooney Viscosity

ASTM D1646

MPP16

ML1+4 @ 100°C

37 – 47

Bound Styrene

ASTM D5775

MPP5-MPP6

wt %

N/A

Block styrene

ASTM D3314

MPP8

wt %

N/A

Solution viscosity*

ASTM D5774

MPP9

cPs

N/A

Gel content

MPP12

arbitrary

N/A

Molecular weight

MPP1

KDalton

N/A

Coupling efficiency

MPP1

%

N/A

Volatile matter content

ASTM D5668

MPP10

wt %

0.3 max

Residual solvent

MPP18

ppm

N/A

Colour

ASTM E313

MPP13

Yellow index

N/A

Solution color (Pt/Co)

ASTM D1209

arbitrary

N/A

Vinyl content

MPP5-MPP6

wt % on butadiene

11 – 13

Ash content

ASTM D5667

MPP15

wt %

0.04

Solvent extractables

ASTM D5774

MPP11

wt %

26.3–29.3

General

Density

ISO 1183

g/cm3

1.04

Water Absorption

ASTM D 570

%

0.3

Rheological

Melt Flow Rate (MFR)

ISO 1133

g/10min

5

Mechanical

Tensile Strength

50 mm/min

ASTM D 638

MPa

35

Strain at break

50 mm/min

ASTM D 638

%

45

Flexural Strength

2 mm/min

ASTM D 790

MPa

68

Flexural Modulus

2 mm/min

ASTM D 790

MPa

2300

Izod Impact Strength Notched

+23°C – thickness 3.2 mm

ISO 180/4A

J/m

280

0°C – thickness 3.2 mm

ISO 180/4A

J/m

190

– 20°C – thickness 3.2 mm

ISO 180/4A

J/m

150

– 40°C – thickness 3.2 mm

ISO 180/4A

J/m

125

+23°C – thickness 4 mm

ISO 180/1A

kJ/m²

20

– 40°C – thickness 4 mm

ISO 180/1A

kJ/m²

10

Charpy Impact Strength, Notched

+23°C

DIN 53453

kJ/m²

16

Unnotched

+23°C

DIN 53453

kJ/m²

NB

Unnotched

– 40°C

DIN 53453

kJ/m²

NB

Rockwell Hardness

scale R

ISO 2039/2

kJ/m²

R110

Thermal

Vicat Softening Tempreture

10 N – 120°C/h

ISO 306/A120

ºC

108

50 N – 120°C/h

ISO 306/B120

ºC

104

Deflection temp. under load (annealed)

1.8 MPa – 120°C/h

ASTM D 648

ºC

104

Ceofficient of linear thermal expansion

ASTM D 696

10 -5/ºC

9

Thermal Conductivity

ASTM C 177

W/(Km)

0.17

Moulding Shrinkage

ISO 294.4

%

0.4-0.6

Flammability

Flame behavior

thickness 1.5 mm

UL 94

class

HB

Glow wire test

thickness 3 mm

IEC 60695-2-1

ºC

650

Electrical

Surface resistivity

dry

IEC 60093

ohm

10+14

Volume resistivity

dry

IEC 60093

ohm*cm

10+15

Dielectric strength

dry

IEC 60243

kV/mm

30

Dielectric constant (relative permittivity)

1000 Hz – dry

IEC 60250

3.1

Dissipation factor

1000 Hz – dry

IEC 60250

15*10-³

General

Mooney Viscosity

ASTM D1646

MPP16

ML1+4 @ 100°C

N/A

Bound Styrene

ASTM D5775

MPP5-MPP6

wt %

34 – 38

Block styrene

ASTM D3314

MPP8

wt %

100

Solution viscosity*

ASTM D5774

MPP9

cPs

N/A

Gel content

MPP12

arbitrary

N/A

Molecular weight

MPP1

KDalton

245 – 275

Coupling efficiency

MPP1

%

85 min

Volatile matter content

ASTM D5668

MPP10

wt %

1 max

Residual solvent

MPP18

ppm

< 10

Colour

ASTM E313

MPP13

Yellow index

15 max

Solution color (Pt/Co)

ASTM D1209

arbitrary

N/A

Vinyl content

MPP5-MPP6

wt % on butadiene

10.0 – 14.0

Ash content

ASTM D5667

MPP15

wt %

N/A

Solvent extractables

ASTM D5774

MPP11

wt %

N/A

General

Mooney Viscosity

ASTM D1646

MPP16

ML1+4 @ 100°C

60 – 80

Bound Styrene

ASTM D5775

MPP5-MPP6

wt %

9.0 – 11.0

Block styrene

ASTM D3314

MPP8

wt %

4 – 6

Solution viscosity*

ASTM D5774

MPP9

cPs

N/A

Gel content

MPP12

arbitrary

N/A

Molecular weight

MPP1

KDalton

N/A

Coupling efficiency

MPP1

%

N/A

Volatile matter content

ASTM D5668

MPP10

wt %

0.75 max

Residual solvent

MPP18

ppm

N/A

Colour

ASTM E313

MPP13

Yellow index

N/A

Solution color (Pt/Co)

ASTM D1209

arbitrary

N/A

Vinyl content

MPP5-MPP6

wt % on butadiene

9.0 – 11.0

Ash content

ASTM D5667

MPP15

wt %

0.2 max

Solvent extractables

ASTM D5774

MPP11

wt %

N/A

General

Mooney Viscosity

ASTM D1646

MPP16

ML1+4 @ 100°C

45 – 55

Bound Styrene

ASTM D5775

MPP5-MPP6

wt %

N/A

Block styrene

ASTM D3314

MPP8

wt %

N/A

Solution viscosity*

ASTM D5774

MPP9

cPs

35 – 50

Gel content

MPP12

arbitrary

4 max

Molecular weight

MPP1

KDalton

N/A

Coupling efficiency

MPP1

%

N/A

Volatile matter content

ASTM D5668

MPP10

wt %

0.75 max

Residual solvent

MPP18

ppm

N/A

Colour

ASTM E313

MPP13

Yellow index

N/A

Solution color (Pt/Co)

ASTM D1209

arbitrary

10 max

Vinyl content

MPP5-MPP6

wt % on butadiene

11 – 13

Ash content

ASTM D5667

MPP15

wt %

0.2 max

Solvent extractables

ASTM D5774

MPP11

wt %

N/A

General

Density

ISO 1183

g/cm3

1.04

Water Absorption

ASTM D 570

%

0.3

Rheological

Melt Flow Rate (MFR)

ISO 1133

g/10min

6

Mechanical

Tensile Strength

50 mm/min

ASTM D 638

MPa

43

Strain at break

50 mm/min

ASTM D 638

%

45

Flexural Strength

2 mm/min

ASTM D 790

MPa

65

Flexural Modulus

2 mm/min

ASTM D 790

MPa

2300

Izod Impact Strength Notched

+23°C – thickness 3.2 mm

ISO 180/4A

J/m

200

0°C – thickness 3.2 mm

ISO 180/4A

J/m

165

– 20°C – thickness 3.2 mm

ISO 180/4A

J/m

125

– 40°C – thickness 3.2 mm

ISO 180/4A

J/m

100

+23°C – thickness 4 mm

ISO 180/1A

kJ/m²

17

– 40°C – thickness 4 mm

ISO 180/1A

kJ/m²

9

Charpy Impact Strength, Notched

+23°C

DIN 53453

kJ/m²

12

Unnotched

+23°C

DIN 53453

kJ/m²

NB

Unnotched

– 40°C

DIN 53453

kJ/m²

NB

Rockwell Hardness

scale R

ISO 2039/2

kJ/m²

R110

Thermal

Vicat Softening Tempreture

10 N – 120°C/h

ISO 306/A120

ºC

114

50 N – 120°C/h

ISO 306/B120

ºC

108

Deflection temp. under load (annealed)

1.8 MPa – 120°C/h

ASTM D 648

ºC

108

Ceofficient of linear thermal expansion

ASTM D 696

10 -5/ºC

9

Thermal Conductivity

ASTM C 177

W/(Km)

0.17

Moulding Shrinkage