TJPC 1500

 

TJPC 1500 

 TJPC 1500

 

1 product description

Styrene-Butadiene Rubber “TJPC 1500” is produced by a technology of cold emulsion copolymerization based on soaps of rosin and fatty acids and contains 23.5% of chemically bonded styrene. It is coagulated by a system of acid and synthetic coagulant and stabilized by a staining antioxidant.

2 applications

TJPC 1500 is appropriate for rubber compounds used in the production of car tires, conveyor belts, footwear, cables, hosepipes and various technical rubber articles.

3 CHARACTERSTICS

TJPC 1500 has very good properties such as process ability, abrasion resistance, and fewer tendencies to scorching.

4 PACKAGING – TRANSPORTATION – STORAGE

35 ±0.5 KG bales wrapped with polyethylene film.

36 bales per crate (1260±18 KG).

TJPC1500 is typically transported in covered road trucks, in covered railway carriages and in standard shipping containers. TJPC 1500 is not a dangerous material to transport.

Product should be stored in sheltered conditions away from direct sunlight away from radiant heating elements and the temperature should not exceed 30°C.

Typical Properties  Units Values Test method
Raw Mooney viscosity MU 46-58 ASTM D1646
Volatile Material % wt < 0.75 ASTM D5668
Ash Content % wt < 1.5 ASTM D5667
Organic acids % wt 4.75 -7.5 ASTM D5774
Soaps % wt < 0.5 ASTM D5774
Bounded styrene % wt 22.5-24.5 ASTM D5775
Compound Mooney viscosity2 MU <84 ASTM D1646
Tensile strength (35 min cured)2 kg/cm2 >250 ASTM D 412
Ultimate elongation (35 min cured)2 % >470 ASTM D 412
300 % Modulus (35 min cured)2 kg/cm2 119-159 ASTM D 412

1 The above data is only a typical value and to each shipping lot/ delivery a quality certificate including data on properties of the product determined during release control is issued. Scope of the testing which is covered by the quality certificate is each time agreed upon in the sales contract.

2 Compounding formula accordinc ASTM D-3182 & D-3185.